PRODUCT DETAILS
1) Material: casting iron, forged steel;
2) Surface treatment: nitrided, hardening nitrided, polished;
3) The characteristics: wear resistance, good strength, and hardness;
The main composition of nodular alloy casting iron crankshaft |
Material components |
The proportion |
Fe |
90% |
C |
3.7~3.8% |
Si |
2.1~2.4% |
Mn |
0.2~0.3% |
P |
0.06% |
S |
0.03~0.06% |
4) Generally crankshaft process: Blank-Quenching and tempering-Shot-blast-Rough machining-Shot
blasting-Heat treatment-Finish machining-Fine grinding-Surface treatment-Polishing-Finished product;
5) Crankshaft quenching hardening;
6) Identify ways of forged steel and casting iron crankshaft:
a: Appearance: casting iron crankshaft appearance is more rough than forged steel crankshaft;
b: Percussive sound: forged steel crankshaft tapping sound is more ringing & echo is longer;
c: Material chemical analysis;
d: Product weight: casting iron crankshaft is lighter than forged steel crankshaft
(the density of casting iron is 7.2 & 7.8 for forged steel).
STRONG CAPABILITY
1) Production: more than 300000pcs/month;
2) Certification: ISO16949, ISO9001, Ts16949, ISO14001, etc.;
3) Overseas sales: ANGOLA branch;
4) Brand: XYTOSAN, OSVAT, GPM, PAGZD, GEO, KOSFA, etc.;
5) MOQ: 1pc if have stocks;
6) TOYOTA Engine Crankshaft
2R, 5R, 12R, 22R, 1Z, 2Z, 11Z, 12Z, 13Z, 14Z, 1DZ, 1AZ, 2AZ, 1ZZ, 2H, 3P, 4P, B, 2B, 3B, 11B, 13B,
14B, 15B, 2J, 2L, 2LT, 3L, 3L-E, 5L, 5L-E, 1E, 2E, 3E, 4E, 5E, 1C, 2C, 1RZ, 2RZ, 3RZ, 1KZ, 1KE-TE,
1Y, 2Y, 3Y, 4Y, 4A, 4A-FE, 5A, 7A, 8A, 3S, 5A, 3K, 4K, 5K, 1KD, 2KD, 1HZ, 1HD-T, 1FZ, 2TR, etc.
TOYOTA |
5R |
13411-44900,13411-49167 |
12R |
13411-31902,13411-31011 |
22R |
13411-38010 |
1Z |
13411-78300-71 |
2Z |
|
11Z |
13411-78760-71 |
12Z |
|
13Z |
|
14Z |
|
1DZ |
|
1AZ |
13401-28010 |
2AZ |
13401-28030 |
1ZZ |
13401-22020 |
1NZ |
13401-21020,13401-0C010 |
2H |
13401-76011-71 |
3P/4P |
13411-7600171 |
B |
13401-56020,6or8 Hole |
2B |
6or8 Hole |
3B |
13401-58010 |
11B/13B |
13401-58020/13401-58018 |
14B |
13401-58030/58021/58050 |
15B |
|
2J |
13411-96100 |
2L |
13401-54040 |
2LT |
|
3L |
13401-54020/54060/54080/54100 |
3L-E |
|
5L |
13401-54061 |
5L-E |
|
1E/2E |
13401-11050 |
3E |
|
4E |
|
5E |
13401-11040 |
1C/2C |
13411-64908 |
1RZ/2RZ |
|
3RZ |
|
1TR/2TR |
13401-75020 |
1KZ |
6or8 Hole |
1Y |
13411-72010 |
2Y |
|
3Y/4Y |
13411-73010 |
4A |
13411-16900 |
4A-FE |
|
5A |
13411-15900 |
7A/8A |
|
3S |
|
5S |
13401-74010 |
3K/4K/5K |
13411-76006-71 |
1KD |
13401-30020/30030/30040/30050 |
2KD |
|
1HZ/1HD-T |
13411-17012 |
1FZ |
13401-66021 |
7) Other Models
BUICK, CHEVY, OPEL, VW, SCANIA, CAT, PERKINS, WEICHAI, MAN, DAEWOO, TOYOTA, ETC.;
ISUZU |
CATERPILLAR(CAT) |
JELCZ |
BENZ |
DEUTZ |
BEDFORD |
MITSUBISHI |
MAZDA |
LADA |
TOYOTA |
KIA |
IFA |
NISSAN |
DAEWOO |
VOLVO |
SUZUKI |
HYUNDAI |
SCANIA |
DAIHATSU |
IVECO |
VW(Volkswagen) |
HINO |
FIAT |
GM |
PEUGEOT |
KAMAS |
CHEVROLET |
KUBOTA |
CLAAS |
OPEL |
YANMAR |
STEYR(STR) |
FORD |
KOMATSU |
IKARUS |
PERKINS |
CUMMINS |
MAN |
... |
Our casting iron crankshaft are made of high quality nodular cast iron, All the products after heat treatment and three shot blast, The lowest strength is for QT700-2, mostly to QT800-3 surface polishing treatment were performed |
8) Other Parts
connecting rod, main bearing, con. rod bearing, camshaft, cylinder liner, cylinder head, cylinder
block, etc..
SERVICE
1) Offering sample before production;
2) Quality guarantee: one year;
3) Making laser logo upon customers' needs;
4) Developing new models according to samples or drawings;
PACKAGE & SHIPPING
1) Neutral packing, or according to customers' requirements;
2) Delivery time: 3 days if have stocks & 35 days for producing;
3) Transportation: by sea or by air(TNT, DHL, FEDEX, UPS, ETC. ).
CONTACT US
ANQING XINYI AUTO PARTS CO., LTD WEB: www.osvat.cn http://xytosan.en.made-in-china.com Address: NO. 80, TIANZHUSHAN ROAD, ANQING CITY, ANHUI PROVINCE, PRC.
Contact: Seven Chen TEL: +86-556-5171 008 FAX: +86-556-5171 000 |